Table 2.
Statistics of the properties captured in the database.
| Property | count | unique | mean | std | min | max |
|---|---|---|---|---|---|---|
| Alloy composition | 1545 | 630 | — | — | — | — |
| Processing method | 1426 | 5 | — | — | — | — |
| Microstructure | 1402 | 40 | — | — | — | — |
| grain size (μm) | 237 | 176 | 90.2 | 183.0 | 0.018 | 2000.0 |
| Exp. Density (g/cm3) | 112 | 52 | 7.6 | 2.5 | 1.46 | 13.6 |
| Calculated Density (g/cm3) | 1545 | 82 | 8.0 | 1.8 | 1.4 | 13.7 |
| Test temperature (°C) | 1364 | 68 | 228.8 | 379.1 | −268.8 | 1600.0 |
| HV | 530 | 372 | 478.3 | 212.9 | 94.7 | 1183.0 |
| YS (MPa) | 1067 | 715 | 891.0 | 569.5 | 24.0 | 3416.0 |
| UTS (MPa) | 535 | 438 | 1184.6 | 721.3 | 80.0 | 4023.6 |
| Elongation (%) | 619 | 245 | 30.2 | 22.0 | 0.0 | 105.0 |
| Elongation plastic (%) | 149 | 85 | 20.3 | 25.7 | 0.0 | 189.2 |
| Exp. Young modulus (GPa) | 145 | 116 | 125.0 | 56.9 | 16.6 | 240.0 |
| Calculated Young modulus (GPa) | 729 | 113 | 166.4 | 48.9 | 72.0 | 298.0 |
| O content (wppm) | 57 | 10 | 764.0 | 2085.0 | 80.0 | 7946.0 |
| N content (wppm) | 45 | 1 | 5.0 | 0.0 | 5.0 | 5.0 |
| C content (wppm) | 4 | 4 | 19911.8 | 16142.8 | 1900.0 | 36380.0 |
Including mean, standard deviation (std) and the minimum (min) and maximum (max) values.