Table 2.
Average PS, GT, EE%, Q6, PDI and ZP for the Prepared DLX in situ Cubo-Gels
| Formula | PS ± SD (nm) (Y1) | GT (oC) (Y2) | EE% ± SD (%) (Y3) | Q6 (%) (Y4) | PDI ± SD | ZP ± SD (mV) |
|---|---|---|---|---|---|---|
| F1 | 239 ± 3 | 80 ± 2 | 93.16 ± 2.84 | 34.87 ± 2.8 | 1 ± 0.1 | 6.1 ± 1.01 |
| F2 | 290 ± 5 | 80 ± 2 | 97.93 ± 0.9 | 26.9 ± 3.65 | 0.459 ± 0.04 | 2.33 ± 0.58 |
| F3 | 276.1 ± 6.24 | 50 ± 4.58 | 97.3 ± 1.28 | 36.53 ± 4.97 | 0.582 ± 0.03 | 4 ± 2.08 |
| F4 | 145.8 ± 4.8 | 34 ± 2 | 98.57 ± 0.51 | 26.43 ± 2.25 | 1 ± 0.1 | 1.6 ± 0.21 |
| F5 | 253 ± 2.65 | 36 ± 2 | 99.68 ± 0.49 | 64.5 ± 4.13 | 0.274 ± 0.02 | 1.6 ± 0.08 |
| F6 | 384.9 ± 4.56 | 80 ± 5 | 96.9 ± 0.07 | 31.97 ± 4.54 | 0.508 ± 0.07 | 9.4 ± 0.51 |
| F7 | 373.4 ± 2.65 | 50 ± 3 | 97.3 ± 0.61 | 29.83 ± 4.38 | 0.409 ± 0.04 | 7.8 ± 1.35 |
| F8a | 307.5 ± 6.61 | 45 ± 1 | 98.56 ± 0.6 | 38 ± 2.36 | 0.365 ± 0.03 | 10.6 ± 1.8 |
| 348.1 ± 4.36 | 45 ± 2 | 98.14 ± 1 | 39.5 ± 2.21 | 0.317 ± 0.02 | 8.33 ± 1.15 | |
| 285 ± 5 | 45 ± 1.63 | 98.1 ± 1.01 | 37.07 ± 5.33 | 0.33 ± 0.03 | 9.87 ± 1.32 | |
| 271.5 ± 4.44 | 45 ± 3 | 98.03 ± 0.25 | 38.7 ± 1.67 | 0.297 ± 0.04 | 8.2 ± 3.79 | |
| 325.9 ± 5.08 | 45 ± 3.61 | 98.1 ± 1 | 36.2 ± 4.55 | 0.281 ± 0.04 | 9.7 ± 3.79 | |
| 317.1 ± 3.49 | 45 ± 2 | 98.1 ± 0.7 | 39.8 ± 2.71 | 0.32 ± 0.03 | 8.9 ± 2 | |
| F9 | 331.4 ± 4.61 | 50 ± 2 | 99.03 ± 0.75 | 37.9 ± 3.29 | 0.222 ± 0.02 | 8.2 ± 3.7 |
| F10 | 366.8 ± 8.61 | 34 ± 2.65 | 98.36 ± 0.58 | 35.53 ± 1.76 | 0.4865 ± 0.01 | 10 ± 1.57 |
| F11 | 377 ± 2.65 | 80 ± 5 | 98.13 ± 0.52 | 49.4 ± 1.01 | 0.431 ± 0.03 | 10.5 ± 1.53 |
| F12 | 515.9 ± 5.29 | 80 ± 2.65 | 99 ± 0.52 | 25.7 ± 2.82 | 0.675 ± 0.02 | 6.87 ± 1.69 |
| F13 | 471.6 ± 2.89 | 52 ± 2.65 | 99 ± 0.2 | 31.87 ± 3.31 | 0.482 ± 0.02 | 9.1 ± 2.85 |
| F14 | 266 ± 6.24 | 32 ± 1 | 99.07 ± 0.54 | 20.3 ± 2.14 | 0.496 ± 0.02 | 6.67 ± 3.06 |
| F15 | 352.7 ± 7.25 | 37 ± 2.65 | 99.3 ± 0.38 | 30.63 ± 1.46 | 0.794 ± 0.02 | 7.6 ± 1.25 |
Note: aF8 represents the center point formulation and its five repetitions.