Table 4.
Contact angle and mechanical characterization of other coating systems.
| Ref. | Coating Type |
Contact Angle (Water) |
Cross Cut Adhesion (ASTM3359-09e2) |
Dolly-Pull Off Adhesion Test (MPa) |
|---|---|---|---|---|
| [47] 1 | polyacrylate-g-polysiloxane | 98° | 5B | - |
| [58] 2 | urethane methacrylates | 109° | 5B 5B |
- |
| [59] 3 | fluorinated/silanized polyacrylates amphiphilic polymers | 116° | 5B | - |
| [60] 4 | PFPE/PDMS/acrylic | 107 ± 0.6 | 5B (on glass) | - |
| [61] | acrylic resin loaded with reduced graphene oxide and cuprous oxide | 113 | 5B (Class 1) |
3.69 |
| [62] | Copolymer systems based on PVA and MMA | - | - | 4 |
| [63] | HPAPD-PMMAb-PHEMA (dopamine, poly(methyl methacrylate) and poly(2-hydroxyethyl methacrylate) | 52 | - | - |
| [64] | dopamine (HPAPD), p-phenylenediamine (PPD), polyaniline (PANA), 3-aminopropyltriethoxysilane (APTS), 3-mercaptopropyltriethoxysilane (MPTS), vinyltrimethoxysilane (VTMS) and octyltrimethoxysilane (OTMS) | 132 | - | - |
| [65] 5 | polysilazane loaded with poly(tetrafluoroethylene) (PTFE) particles | 86° | 5B | 12.7 |
| [66] 6 | Chitosan + starch | - | 2B | - |
| [67] 7 | Fluorinated copolymers and poly(urea-formaldehyde) | 162.3 ± 3.2 | - | - |
1 Surface roughness: 0.068 micron, Pencil hardness test: 6H. 2 Pencil hardness test: 4H, Contact angle in hexadecane: 59°. 3 Hardness: HB. 4 Modulus: 22.16 MPa. 5 Contact angle in diiodomethane: 49.8°. 6 Lap shear test: on Metal 38.3 N, on plastic 200 N, on glass plastic, acrylic, ceramic 4B, on metal 2B. 7 Contact angle after 16 abrasion cycles: 150 ± 3.2, Cross cut adhesion test: good on glass after 20th cross cut tape test.