Table 2.

The β phase content at room temperature of selected specimens as determined using electron backscatter diffraction (EBSD), uncertainty is ±0.5%. The average relative density of samples of the same metallurgical state is shown in the right column.

Metallurgical State	β Phase Content [%]	Relative Density [%]
As Built	<1	99.89 ± 0.03
HIP 780 °C	1.25	99.98 ± 0.02
HIP 920 °C	3.2	99.98 ± 0.04
HT 1000 °C	7	99.91 ± 0.01