Table 3.

Energy dispersive spectroscopy (EDS) results of two spots in as-built sample (Figure 3a) and of three spots in HIP-920 sample, bright, dark and mixed area (Figure 4d).

Measured Phase	Aluminum [wt %]	Vanadium [wt %]	Iron [wt %]	Titanium [wt %]
AB—Bright Phase (1)	6.58	7.05	0.51	85.86
AB—Dark Phase (2)	6.04	5.26	0.27	88.44
HIP 920 °C—Bright Phase (1)	5.41	9.03	0.25	85.31
HIP 920 °C—Dark Phase (2)	6.60	3.25	Not detected	90.15
HIP 920 °C—Mixed Phase (3)	6.12	6.78	Not detected	87.10