Table 1.

Summary of the features present in both datasets, including feature name, description, units, mean values, and standard deviations.

Feature name	Description	Unit	9–12% Cr FMA		Austenitic stainless steel
			Mean	Std.	Mean	Std.
Fe	Iron content	wt%	85.92	6.47	56.06	18.53
C	Carbon content	wt%	0.14	0.04	0.06	0.02
Cr	Chromium content	wt%	9.98	1.45	18.25	1.74
Mn	Manganese content	wt%	0.44	0.17	1.30	0.44
Si	Silicon content	wt%	0.25	0.16	0.52	0.14
Ni	Nickel content	wt%	0.28	0.23	21.76	18.41
Co	Cobalt content	wt%	0.72	1.44	0.14	0.26
Mo	Molybdenum content	wt%	0.84	0.52	1.09	1.88
W	Tungsten content	wt%	0.57	0.81	0.03	0.14
Nb	Niobium content	wt%	0.05	0.06	0.15	0.29
Al	Aluminum content	wt%	0.01	8.69 × 10−3	0.11	0.16
P	Phosphorous content	wt%	0.01	8.65 × 10−3	0.02	8.11 × 10−3
Cu	Copper content	wt%	0.06	0.16	0.21	0.49
Ti	Titanium content	wt%	4.4 × 10−3	0.02	0.16	0.19
Ta	Tantalum content	wt%	0.04	0.09
Hf	Hafnium content	wt%	3.99 × 10−3	7.98 × 10−3
Re	Rhenium content	wt%	1.33 × 10−3	0.01
V	Vanadium content	wt%	0.17	0.09	4.24 × 10−3	0.01
B	Boron content	wt%	4.05 × 10−3	4.62 × 10−3	8.82 × 10−4	9.65 × 10−4
N	Nitrogen content	wt%	0.03	0.02	0.03	0.05
O	Oxygen content	wt%	1.93 × 10−3	6.89 × 10−3
S	Sulfur content	wt%	4.75 × 10−3	3.84 × 10−3	9.00 × 10−3	5.79 × 10−3
Zr	Zirconium content	wt%	3.8 × 10 − 5	1.92 × 10−4
Homo	Homogenization	Yes/no
Normal	Normalization or austenization heat treatment temperature	℃	1075.46	77.77	1115.09	64.39
Temper1	Temper heat treatment 1	℃	685.49	75.61
AGS no	Austenitic grain size number	$\frac{\mathit{grains}}{{\text{mm}}^2}$	6.49	2.34	4.76	1.55
TT_Temp	Test temperature	℃	369	229	477	269
TT_EL	Elongation to failure	%	25.61	13.04	52.31	18.21
TT_RA	Reduction in area	%	71.54	14.51	69.35	12.12