Table 8.
Mechanical properties of the cured resins.
| Sample | Tensile Properties | Flexural Properties | |||
|---|---|---|---|---|---|
| Strength (MPa) | Modulus (GPa) | Elongation (%) | Strength (MPa) | Modulus (GPa) | |
| PETI-O | 54.2 (±4.86) | 1.99 (±0.08) | 2.8 (±0.54) | 125.6 (±1.57) | 3.1 (±0.07) |
| PETI-F | 66.2 (±5.67) | 2.40 (±0.10) | 3.1 (±0.60) | 126.2 (±5.39) | 3.6 (±0.08) |
| PETI-P | 64.0 (±5.23) | 2.28 (±0.11) | 2.9 (±0.69) | 132.3 (±8.90) | 3.2 (±0.18) |
| PETI-1 | 62.2 (±5.12) | 1.96 (±0.07) | 3.4 (±0.32) | 136.2 (±6.34) | 3.2 (±0.14) |
| PETI-2 | 50.8 (±6.75) | 2.07 (±0.03) | 2.5 (±0.37) | 128.8 (±7.25) | 3.3 (±0.09) |
| PETI-3 | 56.4 (±3.17) | 2.07 (±0.07) | 2.9 (±0.25) | 137.1 (±7.01) | 3.2 (±0.04) |