. 2021 Mar 30;7(3):e06613. doi: 10.1016/j.heliyon.2021.e06613

Table 4.

Activities of components of liquid Li–Mg alloy at temperatures 1000 K, 1300 K, 1600 K, 1900 K and 2200 K.

X_Mg	Activities
	T = 1000 K
	Linear fit		Expon. fit		Experimental [25]		Wang et al. [19]
	a_Li	a_Mg	a_Li	a_Mg	a_Li	a_Mg	a_Li	a_Mg
0.1	0.866	0.012	0.885	0.018	0.865	0.012	0.893	0.021
0.2	0.690	0.043	0.746	0.048	0.689	0.043	0.763	0.052
0.3	0.510	0.107	0.591	0.097	0.509	0.107	0.609	0.101
0.4	0.353	0.213	0.432	0.174	0.353	0.213	0.449	0.178
0.5	0.232	0.357	0.287	0.287	0.232	0.356	0.303	0.289
0.6	0.146	0.521	0.172	0.437	0.146	0.521	0.186	0.430
0.7	0.090	0.678	0.093	0.608	0.090	0.679	0.103	0.591
0.8	0.053	0.808	0.046	0.771	0.053	0.808	0.050	0.750
0.9	0.027	0.909	0.019	0.900	0.027	0.908	0.019	0.889

Activities
T = 1300 K						T = 1600 K
Linear fit		Expon. fit		Wang et al. [19]		Linear fit		Expon. fit		Wang et al. [19]
a_Li	a_Mg	a_Li	a_Mg	a_Li	a_Mg	a_Li	a_Mg	a_Li	a_Mg	a_Li	a_Mg
0.864	0.016	0.888	0.028	0.895	0.028	0.863	0.019	0.890	0.037	0.897	0.034
0.686	0.061	0.757	0.070	0.773	0.066	0.683	0.075	0.765	0.089	0.779	0.077
0.509	0.150	0.614	0.132	0.630	0.122	0.508	0.185	0.630	0.159	0.643	0.137
0.362	0.283	0.469	0.218	0.479	0.202	0.368	0.338	0.493	0.251	0.499	0.219
0.254	0.437	0.332	0.332	0.336	0.312	0.270	0.496	0.364	0.364	0.359	0.328
0.179	0.584	0.217	0.471	0.216	0.448	0.203	0.627	0.250	0.495	0.237	0.460
0.126	0.706	0.129	0.622	0.125	0.600	0.156	0.724	0.157	0.634	0.142	0.607
0.084	0.808	0.068	0.769	0.063	0.752	0.112	0.807	0.087	0.771	0.073	0.754
0.044	0.902	0.028	0.895	0.024	0.888	0.059	0.898	0.037	0.894	0.028	0.888

T = 1900 K						T = 2200 K
Linear fit		Expon. fit		Wang et al. [19]		Linear fit		Expon. fit		Wang et al. [19]
a_Li	a_Mg	a_Li	a_Mg	a_Li	a_Mg	a_Li	a_Mg	a_Li	a_Mg	a_Li	a_Mg
0.863	0.022	0.892	0.044	0.898	0.039	0.862	0.024	0.893	0.051	0.898	0.042
0.681	0.087	0.771	0.104	0.783	0.085	0.680	0.097	0.775	0.116	0.786	0.092
0.507	0.213	0.642	0.180	0.653	0.148	0.507	0.237	0.651	0.197	0.660	0.157
0.372	0.381	0.512	0.275	0.513	0.232	0.375	0.417	0.525	0.294	0.523	0.241
0.281	0.541	0.387	0.387	0.375	0.339	0.289	0.577	0.405	0.405	0.388	0.347
0.222	0.658	0.275	0.512	0.253	0.468	0.236	0.682	0.294	0.526	0.265	0.474
0.180	0.737	0.179	0.644	0.154	0.611	0.200	0.746	0.197	0.652	0.164	0.614
0.136	0.807	0.103	0.774	0.081	0.755	0.157	0.807	0.116	0.777	0.087	0.756
0.073	0.895	0.044	0.894	0.032	0.888	0.085	0.893	0.051	0.894	0.034	0.888