Table 1. Reported Conductivity and Stretchability of Screen-Printed Conductors Using Nanomaterials.

ref conductor substrate material loading (wt %) primary solvent sintering conductivity stretchability
(9) AgNP PU 73 terpineol 60 min at 150 °C 3.3 × 104 (S/cm) 8%
(16) AgNP PI 80 HMC 30 min at 220 °C 1.2 × 105 (S/cm)  
(17) AgNP PU 75 tetradecane room temperature 1.97 Ω/sq ∼38%
(4) AgNW PUA (transfer from PET) 6.6 HMC 15 min at 150 °C 4.67 × 104 (S/cm) ∼70%
(20) AgNW PDMS 2 terpineol photonic (laser 0.67 ms, 9 W) 1.9 Ω/sq ∼20%
(21) AgNW PDMS 70 terpineol 2 h at 80 °C 6.9 × 104 (S/cm) ∼100%
(24) MWCNT silicone 7.5 ethanol room temperature 0.5–1.3 Ω/sq  
(25) Ag/MWCNT PI 0.6 (CNT) not mentioned, added SDS 20 min at 120 °C 7.26 μΩ/sq