Table 3.

Mechanical properties of the decellularized samples

Group	Ultimate stress (MPa)	Ultimate strain (%)	Elastic modulus (MPa) (Young’s Modulus)
Control 1	5.44 ± 0.65	0.38 ± 0.04	34.35 ± 5.33
T3–15	6.96 ± 0.23	0.51 ± 0.02	31.32 ± 1.43
T3–30	6.52 ± 0.15	0.48 ± 0.07	30.12 ± 2.54
T5–15	6.13 ± 0.74	0.45 ± 0.06	28.63 ± 4.29
T5–30	5.94 ± 0.52	0.41 ± 0.01	27.43 ± 5.41
S3–15	3.97 ± 0.91	0.25 ± 0.06	18.121 ± 4.32
S3–30	3.51 ± 0.23	0.21 ± 0.01	16.64 ± 7.12
S5–15	2.91 ± 0.12	0.18 ± 0.05	14.23 ± 4.32
S5–30	2.51 ± 0.43	0.16 ± 0.06	13.56 ± 8.32
ST3–15	5.16 ± 0.38	0.38 ± 0.02	25.23 ± 1.39
ST3–30	4.95 ± 0.71	0.35 ± −0.030	22.23 ± 4.82
ST5–15	4.51 ± 0.39	0.31 ± 0.05	21.12 ± 5.43
ST5–30	4.29 ± 0.65	0.29 ± 0.04	19.84 ± 3.54

Mechanical tensile data are expressed as means ± SD, n = 3