Table 1.
Selected properties of low density polyethylene Malen E FABS 23-D022 [74].
| Property | Value | Unit |
|---|---|---|
| Density | 923 | kg/m3 |
| MFR (190 °C/2.16 kg) | 1.95 | g/10 min |
| Vicat softening temperature (50 °C/h, 10 N) | 91 | °C |
| Melting temperature | 112 | °C |
| Content of polymer anti-blocking | 0.017 | % |
| Slip agent content (oleamide) | 0.05 | % |
| Tensile strength in longitudinal direction * | 18 | MPa |
| Tensile strength in transverse direction * | 17 | MPa |
| Strain at break in longitudinal direction * | 450 | % |
| Strain at break in transverse direction * | 540 | % |
| Puncture resistance (EN ISO 7765-1) * | 190 | G |
| Haze (ASTM D 1003) * | 8 | % |
* The values were determined for a film with a thickness of 50 µm, extruded at a temperature of 180 °C and a blow-up ratio of 1:2.5.