Syntheses and textural porosities of the ATZ samples.
Sample | x a | y a | Si/Tic | S BET d (m2 g−1) | S micro d (m2 g−1) | S ext d (m2 g−1) | V total e (cm3 g−1) | V micro d (cm3 g−1) | V meso f (cm3 g−1) | I 960/800 g |
---|---|---|---|---|---|---|---|---|---|---|
ATZ-TEA | 0.50 | 10 | 40.8 | 605 | 352 | 253 | 1.89 | 0.14 | 1.75 | 2.17 |
ATZ-TEA-5b | 0.50 | 10 | 4.9 | 623 | 283 | 340 | 2.05 | 0.12 | 1.93 | 2.97 |
ATZ-TMAda | 0.50 | 10 | 40.7 | 747 | 319 | 428 | 1.93 | 0.13 | 1.80 | 1.93 |
ATZ-PhHE | 0.25 | 30 | 41.3 | 537 | 318 | 219 | 1.40 | 0.14 | 1.26 | 2.31 |
ATZ-DPhHE | 0.25 | 30 | 41.2 | 730 | 628 | 102 | 0.41 | 0.25 | 0.16 | 2.13 |
ATZ-PhDC | 0.25 | 30 | 40.5 | 498 | 299 | 199 | 1.76 | 0.13 | 1.63 | 1.89 |
Initial gel: SiO2: 0.025TiO2: xOSDA: yH2O.
Prepared with TiO2/SiO2 = 0.2.
Measured by inductively coupled plasma (ICP).
Specific surface area calculated from the nitrogen adsorption isotherm using the BET method. Smicro (micropore area), Sext (external surface area), and Vmicro (micropore volume) calculated using the t-plot method.
Total pore volume at P/P0 = 0.995.
V meso = Vtotal − Vmicro.
FT-IR relative intensity of the bands at 960 and 800 cm−1.