Table 1.
Dielectric properties of the platinum-cured silicone relative to the concentrations of Slacker and Thi-vex.
| Thi-Vex Concentration (%) | |||||||||
|---|---|---|---|---|---|---|---|---|---|
| 0.0 | 0.5 | 1.0 | 2.0 | ||||||
| ε’ (F/m) | σ (S/m) | ε’ (F/m) | σ (S/m) | ε’ (F/m) | σ (S/m) | ε’ (F/m) | σ (S/m) | ||
| Silicone:Slacker ratio | 1:0.00 | 3.5329 ± 0.0672 | 0.000284 ± 0.000021 | 3.3872 ± 0.3338 | 0.000381 ± 0.000197 | 3.5309 ± 0.0633 | 0.000441 ± 0.000133 | 3.4346 ± 0.2649 | 0.000622 ± 0.000033 |
| 1:0.25 | 3.4443 ± 0.0861 | 0.000303 ± 0.000050 | 3.4641 ± 0.0417 | 0.000322 ± 0.000042 | 3.4621 ± 0.1472 | 0.000360 ± 0.000188 | 3.5533 ± 0.1595 | 0.000455 ± 0.000318 | |
| 1:0.50 | 3.4346 ± 0.0051 | 0.000226 ± 0.000009 | 3.4202 ± 0.0592 | 0.000264 ± 0.000091 | 3.4424 ± 0.1290 | 0.000309 ± 0.000263 | 3.5621 ± 0.1954 | 0.000504 ± 0.000358 | |
| 1:0.75 | 3.3788 ± 0.0776 | 0.000229 ± 0.000135 | 3.4716 ± 0.0062 | 0.000318 ± 0.000054 | 3.4101 ± 0.1122 | 0.000208 ± 0.000166 | 3.3851 ± 0.1859 | 0.000310 ± 0.000275 | |
| 1:1.00 | 3.3147 ± 0.0613 | 0.000261 ± 0.000051 | 3.4197 ± 0.0466 | 0.000302 ± 0.000030 | 3.3960 ± 0.1110 | 0.000282 ± 0.000204 | 3.4019 ± 0.1394 | 0.000313 ± 0.000240 | |
| 1:1.25 | 3.3101 ± 0.0125 | 0.000195 ± 0.000005 | 3.3467 ± 0.0092 | 0.000305 ± 0.000070 | 3.3452 ± 0.0941 | 0.000276 ± 0.000225 | 3.3871 ± 0.1813 | 0.000322 ± 0.000353 | |
| 1:1.50 | 3.2293 ± 0.0735 | 0.000226 ± 0.000056 | 3.3035 ± 0.2698 | 0.000307 ± 0.000369 | 3.3171 ± 0.1752 | 0.000191 ± 0.000343 | 3.3341 ± 0.1341 | 0.000241 ± 0.000230 | |
| 1:1.75 | 3.2195 ± 0.1177 | 0.000187 ± 0.000135 | 3.2082 ± 0.1983 | 0.000233 ± 0.000328 | 3.2998 ± 0.1418 | 0.000262 ± 0.000231 | 3.3225 ± 0.1240 | 0.000302 ± 0.000247 | |
| 1:2.00 | 2.8075 ± 0.2730 | 0.00018 ± 0.000255 | 3.1858 ± 0.2625 | 0.000154 ± 0.000288 | 3.2688 ± 0.1410 | 0.000175 ± 0.000187 | 3.2468 ± 0.0649 | 0.000247 ± 0.000174 | |