Table 3.

Compressive moduli of the platinum-cured and condensation-cured silicone relative to % strain and Slacker concentrations.

Sample	Slacker Ratio	Modulus at 2% Strain (kPa)	Modulus at 4% Strain (kPa)	Modulus at 6% Strain (kPa)	Modulus at 8% Strain (kPa)	Modulus at 10% Strain (kPa)
Platinum-cured Silicone	1:0.00	433 ± 37	553 ± 31	768 ± 33	953 ± 36	1045 ± 34
	1:0.25	207 ± 13	240 ± 14	300 ± 16	347 ± 18	368 ± 19
	1:0.50	96 ± 6	111 ± 7	137 ± 8	157 ± 7	166 ± 6
	1.0.75	48 ± 2	53 ± 1	60 ± 1	64 ± 1	66 ± 1
	1:1.00	16 ± 1	17 ± 1	18 ± 1	20 ± 1	21 ± 1
	1:1.25	14 ± 1	14 ± 1	15 ± 1	16 ± 1	17 ± 2
Condensation-cured Silicone	N/A	220 ± 15	261 ± 15	349 ± 18	442 ± 20	489 ± 21