Table 1.

The values of the flux of the water-rich permeate through the membranes coated with N-TiO₂/F-SiO₂ with varied compositions that were subjected to sodium dodecyl sulfate (SDS)-stabilized n-hexadecane-in-water emulsion (10:90 vol:vol, n-hexadecane:water) dissolved with salt (1.0 wt% NaCl with respect to the water mass).

N-TiO2/F-SiO2 Compositions	Flux at t = 0 (Jo) (Lm−2h−1kPa−1)	Flux at t = 180 min (Jt) (Lm−2h−1kPa−1)
N-TiO2/F-SiO2 (0)	0.0467	0.0177
N-TiO2/F-SiO2 (20 wt%)	0.0547	0.0163
N-TiO2/F-SiO2 (40 wt%)	0.0627	0.0174
N-TiO2/F-SiO2 (60 wt%)	0.0786	0.0157
N-TiO2/F-SiO2 (80 wt%)	0.0826	0.0135
N-TiO2/F-SiO2 (100 wt%)	0.0826	0.0033