Table 1.

Material parameters defining the constitutive law of SHCC.

${\delta }_{peak}$	(µm)	100
${\delta }_1$	(µm)	1160
$S{F}_1$	(-)	0.40
$S{F}_2$	(-)	0.40
${\delta }_{max}$	(µm)	3000
${\epsilon }_{peak}$	(%)	3.3
${\epsilon }_1$	(%)	38.7
${\epsilon }_{max}$	(%)	100
${\epsilon }_{loc}^f$	(%)	3.3
$L_{ch}^f$	(mm)	3.0
${\sigma }_{fc}$	(MPa)	3.7–10.0
${\sigma }_{peak}$	(MPa)	6.5–12.0
Compressive strength	(MPa)	140
Elastic modulus	(GPa)	29
Poisson’s ratio	(-)	0.2