Table 1.

Physical characteristics of Pel-80A-based electrospun matrices.

Matrix Composition, Condition	Tensile Strength (MPa)	Elongation at Break (%)	Elastic Modulus (MPa)	Elastic Strain (%)	Water Contact Angle (°)
3.5% Pel-80A, dry	6.07 ± 0.32	156 ± 19.8	5.67 ± 0.4	107.5 ± 3.5	115.3 ± 0.2
3.5% Pel-80A, wet	5.03 ± 0.69	142 ± 21.3	4.43 ± 0.34	106.5 ± 3.5	-
3.5% Pel-80A + 5% Gel, dry	8.14 ± 1.19	190 ± 27.5	6.81 ± 0.41	155.5 ± 0.7	112.5 ± 1.5
3.5% Pel-80A + 5% Gel, wet	7.86 ± 0.50	195 ± 20.5	5.45 ± 0.38	126.5 ± 4.9	-
3.5% Pel-80A + 10% Gel, dry	8.41 ± 0.48	192 ± 36.2	5.17 ± 0.43	116 ± 4.5	110.2 ± 1.9
3.5% Pel-80A + 10% Gel, wet	6.77 ± 0.46	124 ± 51.0	3.93 ± 0.08	77 ± 1.4	-
3.5% Pel-80A + 15% Gel, dry	6.76 ± 0.29	125 ± 13.5	5.36 ± 0.33	78 ± 1.2	111.7 ± 3.3
3.5% Pel-80A + 15% Gel, wet	6.05 ± 0.56	122 ± 21.0	5.25 ± 0.46	70 ± 1.4	-