Table 4.

Properties of compacts.

Measured Value	CP [MPa]	Cellactose® 80	CombiLac®	MicroceLac® 100	StarLac®
UM [mg]	78	198.81 ± 1.50	197.66 ± 7.57	199.78 ± 1.35	199.25 ± 0.93
	130	199.20 ± 0.74	198.08 ± 2.75	200.70 ± 0.34	197.73 ± 1.98
	182	196.96 ± 4.35	198.96 ± 2.22	199.51 ± 0.43	196.48 ± 2.57
	78	-	-	-	-
RMS [nm]	130	-	-	-	-
	182	202.13 ± 122.59	196.08 ± 91.94	130.58 ± 76.30	180.85 ± 119.66
PD [g/cm3]	78	1.55088 ± 0.0004	1.54436 ± 0.0001	1.5536 ± 0.0002	1.53477 ± 0.0012
	130	1.54804 ± 0.0004	1.54201 ± 0.0001	1.5501 ± 0.0002	1.53629 ± 0.0009
	182	1.54662 ± 0.0002	1.543001 ± 0.0003	1.5542 ± 0.0002	1.53819 ± 0.0011
Po [%]	78	25.56 ± 2.27	23.45 ± 2.05	23.68 ± 1.21	19.86 ± 1.16
	130	18.66 ± 0.77	15.77 ± 2.34	17.40 ± 1.65	15.06 ± 3.32
	182	15.21 ± 2.86	11.77 ± 1.34	13.23 ± 1.68	13.45 ± 2.01
He [mm]	78	4.46 ± 0.11	4.41 ± 0.09	4.33 ± 0.06	4.28 ± 0.06
	130	4.11 ± 0.03	4.03 ± 0.09	4.02 ± 0.07	3.99 ± 0.15
	182	3.87 ± 0.04	3.83 ± 0.04	3.84 ± 0.07	3.88 ± 0.05
Fr [%]	78	1.83	2.86	0.33	4.79
	130	1.30	3.01	0.15	6.69
	182	3.23	0.83	0.23	5.07
Di [min]	78	0.13 ± 0.00	0.35 ± 0.02	0.27 ± 0.10	0.68 ± 0.07
	130	0.28 ± 0.02	0.37 ± 0.03	1.72 ± 0.70	0.73 ± 0.12
	182	0.48 ± 0.13	0.55 ± 0.03	1.78 ± 0.70	0.72 ± 0.15
T1 [min]	78	0.12 ± 0.00	0.27 ± 0.02	0.70 ± 0.55	0.15 ± 0.02
	130	0.28 ± 0.05	0.25 ± 0.07	0.97 ± 0.33	0.18 ± 0.02
	182	0.97 ± 0.40	0.60 ± 0.35	2.23 ± 1.40	0.15 ± 0.02
T2 [min]	78	0.22 ± 0.03	0.43 ± 0.05	1.25 ± 0.45	0.18 ± 0.00
	130	0.53 ± 0.05	0.65 ± 0.17	2.90 ± 1.32	0.33 ± 0.07
	182	1.65 ± 0.60	1.20 ± 0.55	9.68 ± 5.05	0.28 ± 0.07
WA [%]	78	93.76 ± 3.85	59.59 ± 1.20	63.98 ± 5.75	36.57 ± 4.76
	130	96.65 ± 3.11	66.28 ± 4.65	59.19 ± 5.55	38.83 ± 2.87
	182	101.13 ± 4.75	69.65 ± 2.49	60.90 ± 18.77	37.42 ± 5.28

CP—compression pressure; UM—uniformity of mass; RMS—surface topography and roughness; PD—pycnometric density; Po—porosity of tablets; He—height; Fr—friability; Di—disintegration; T1, T2—wetting time; WA—water absorption ratio.