Table 2.
Details of the systems studied for the molecular dynamics simulations
| Polymer chain | No. of polymer chains/no. of dye molecules | Weight % of coumarin-6 | Weight % of PLGA |
|---|---|---|---|
| 25mer PGA | 1/1 | 19.26 | 80.73 |
| 50mer PGA | 1/1 | 10.71 | 89.28 |
| 100mer PGA | 1/1 | 5.67 | 94.32 |
| 25mer PLA | 1/1 | 16.14 | 83.85 |
| 50mer PLA | 1/1 | 8.82 | 91.17 |
| 100mer PLA | 1/1 | 4.62 | 95.37 |
| 25mer PLGA 25:75 | 1/1 | 18.98 | 81.01 |
| 50mer PLGA 25:75 | 1/1 | 9.81 | 90.18 |
| 100mer PLGA 25:75 | 1/1 | 5.37 | 94.62 |
| 25mer PLGA 50:50 | 1/1 | 18.16 | 81.83 |
| 50mer PLGA 50:50 | 1/1 | 9.34 | 90.65 |
| 100mer PLGA 50:50 | 1/1 | 5.09 | 94.9 |
| 25mer PLGA 75:25 | 1/1 | 17.4 | 82.59 |
| 50mer PLGA 75:25 | 1/1 | 8.9 | 91.09 |
| 100mer PLGA 75:25 | 1/1 | 4.85 | 95.14 |
| 50mer PGA | 3/1 | 3.84 | 96.15 |
| 50mer PGA | 3/3 | 10.71 | 89.28 |
| 50mer PGA | 3/6 | 19.35 | 80.64 |
| 50mer PGA | 3/10 | 28.57 | 71.42 |
| 50mer PLA | 3/1 | 3.12 | 96.87 |
| 50mer PLA | 3/3 | 8.82 | 91.17 |
| 50mer PLA | 3/6 | 16.21 | 83.78 |
| 50mer PLA | 3/10 | 24.39 | 75.60 |
| 50mer PLGA 25:75 | 3/1 | 3.5 | 96.49 |
| 50mer PLGA 25:75 | 3/3 | 9.8 | 90.18 |
| 50mer PLGA 25:75 | 3/6 | 17.88 | 82.11 |
| 50mer PLGA 25:75 | 3/10 | 26.63 | 73.36 |
| 50mer PLGA 50:50 | 3/1 | 3.32 | 96.67 |
| 50mer PLGA 50:50 | 3/3 | 9.34 | 90.65 |
| 50mer PLGA 50:50 | 3/6 | 17.08 | 82.91 |
| 50mer PLGA 50:50 | 3/10 | 25.46 | 74.43 |
| 50mer PLGA 75:25 | 3/1 | 3.15 | 96.84 |
| 50mer PLGA 75:25 | 3/3 | 8.9 | 91.09 |
| 50mer PLGA 75:25 | 3/6 | 16.36 | 83.63 |
| 50mer PLGA 75:25 | 3/10 | 24.58 | 75.41 |