. 2021 Aug 5;8(19):2100774. doi: 10.1002/advs.202100774

Figure 6.

Figure 6

a) Li4SiO4–Li3VO4 partial phase diagram. Reproduced with permission.[ 55 ] Copyright 1984, Elsevier. b) Structural evolutions at PLD deposition at 25 °C and after annealing at 200 °C and 400 °C, respectively. Reproduced with permission.[ 61 ] Copyright 2004, Elsevier. c) Temperature dependence of LVSO electrolytes prepared by bulk, rf‐sputtering, PLD and hydrothermal processes (Kuwata (PLD and Li3.4V0.6Si0.4O4, bulk),[ 60 ] Ohtsuka (Li3.4V0.6Si0.4O4, SP),[ 64 ] Zhao (Li6.16V0.61Si0.39O5.36, PLD at 300 °C),[ 65 ] Tao (Li3.4V0.6Si0.4O4, HT),[ 63 ] and Yamaka (Li3.4V0.6Si0.4O4, bulk),[ 66 ] and d) cyclic voltammogram of LVSO thin film at a scan rate of 10 mV s−1. Reproduced with permission.[ 65 ] Copyright 2003, Elsevier.