Synthetic conditions for colloidal copper nitride NCs.

Precursora	[Cu] (mM)	Solventb/ligandc	Ligand/Cu ratio	Temperature (°C)	Time (min)	Morphology	Phase	Size (nm)	Ref.
Cu(NO3)2·3H2O	101	ODA	32	240	10	Cubic	Cu3N	15	115
Cu(NO3)2·3H2O	101	ODA	32	280	5	Spherical	Cu3N	10	115
Cu(NO3)2·3H2O	101	ODA	32	260 + 240	5 + 5	Spherical	Cu3N	15	115
Cu(NO3)2·3H2O	101	ODA	32	220 + 240	5 + 5	Spherical	Cu3N	15	115
Cu(NO3)2·3H2O	101	ODA	32	220	20	Irregular	Cu3N	50	115
Cu(NO3)2·3H2O		ODA	40	240	10		Cu + Cu3N		115
Cu(NO3)2·3H2O		ODA	13	240	10		CuO + Cu3N		115
Cu(NO3)2·3H2O	24	ODE/ODA	67	250	30	Cubic	Cu3N	26	117
Cu(NO3)2·3H2O	24	ODE/HDA	69	250	30	Cubic	Cu3N	19	117
Cu(NO3)2·3H2O	24	ODE/OLAm	63	250	30	Cubic	Cu3N	11	117
Cu(NO3)2·3H2O	24	OLAm		250	30	Irregular	Cu3N		117
Cu(NO3)2·3H2O	25	ODE/OLAm	31	240	15	Cubic	Cu3N		118
Cu(NO3)2·3H2O + Pd(acac)2	25	ODE/OLAm	31	240	15	Cubic	Cu3PdN	16	118
Cu(NO3)2·3H2O + Pd(acac)2	25	ODE/OLAm	31	190	30	Cubic	Cu3PdN		119
Cu(NO3)2·3H2O	25	ODE/OLAm	31	210	30	Cubic	Cu3N		119
Cu(NO3)2·3H2O	75	ODA/OLAm	45	240	20	Cubic	Cu3N	25	105
Cu(NO3)2·3H2O	88	ODA/OLAm	41	240	30	Cubic	Cu3N	25	103
Cu(NO3)2·3H2O	88	ODA/OLAm	41	250	30	Cubic	Cu3N	20	103
Cu(NO3)2·3H2O	88	ODA/OLAm	41	260	30	Cubic	Cu3N	10	103
Cu(NO3)2·3H2O	88	ODA/OLAm	41	230	30	Spherical	Cu3N	20	103
Cu(NO3)2·5H2O + HMT	50	Hexanol	—	200	60	Spherical	Cu3N	80	122
Cu(acetate)2·H2O + NH3	10	Nonanol	—	190	60	Spherical	Cu3N	200	123
PPC	50	ODA	74	260	5	Spherical	Cu3N	3	124
Cu(NO3)2·3H2O	50	ODA	74	260	5	Cubic	Cu3N	19	124
Cu(OMe)2	92	BnNH2	117	140	15	Spherical	Cu3N	2	125
CuI + KNH2 + NH3	21	Pyridine	—	−35 + 130	10 + 30	Spherical	Cu3N	4	126

^aHMT = hexamethylenetetraamine, PPC = pyrrole-2-carbaldpropyliminato Cu(ii).

^bODE = 1-ODE.

^cODA = octadecylamine, OLAm = oleylamine, HDA = hexadecylamine.