Table 3. Summary of the Coatings.

material	Mna (g/mol)	cross-linker	method	dry content (wt %)	solvent	Tgb (°C)	Tdc (°C)	CAd (deg)	Cobb120e (g/m2)
pVaL2k	1920	HMMM	thermal curing	60	n-butyl acetate	35.1	287.8	86.1	13.7
pVaL4k	3780	HMMM	thermal curing	50	n-butyl acetate	55.6	326.9	80.4	4.1
pVaL8k	6780	HMMM	thermal curing	50	xylenes	44.8	308	84.0	8.1
pHHDC_DMM	6400	TMTP	UV-curing	40	n-butyl acetate	62.0	269.8	72.1	2.7
pHHDC_DMI	8400	TMTP	UV-curing	40	n-butyl acetate	57.7	274.1	82.6	1.1
pHHDC_DMM_FDCA	6100	TMTP	UV-curing	40	n-butyl acetate	47.1	265.4	61.7	2.1
pHHDC_DMI_FDCA	6200	TMTP	UV-curing	40	n-butyl acetate	61.5	267.2	91.8	1.5

^aDetermined by ¹H NMR (compare Tables 1 and 2).

^bDetermined by DSC using the second heating to determine the glass transition temperatures.

^cDetermined by TGA; T_d was defined as the temperature corresponding to 5% weight loss.

^dValues correspond to the average of five measurements.

^eWater absorptiveness is given in g/m²; the Cobb tests were made with inspiration from the official ISO-535 standard but with a decreased test diameter of 3.3 cm.