Table 5.
Tensile test and TGA results for all investigated samples.
| Sample | Elastic Modulus, MPa | Stress at Break, MPa | % Elongation at Break | T97%, °C | Tmax, °C |
|---|---|---|---|---|---|
| PP-AO | 2035 ± 152 | 314 ± 18 | 165 ± 13 | 263 | 303 |
| PP-AO-MA | 2458 ± 235 | 357 ± 26 | 168 ± 12 | 273 | 310 |
| PP-AO-MT | 2183 ± 230 | 340 ± 38 | 159 ± 14 | 290 | 323 |
| PP-AO-MA-MT | 2468 ± 393 | 351 ± 45 | 154 ± 12 | 290 | 329 |
| PP-AO-UT | 2680 ± 368 | 378 ± 36 | 173 ± 10 | 294 | 332 |
| PP-AO-MA-UT | 2206 ± 384 | 394 ± 46 | 176 ± 17 | 297 | 340 |
| PP-AO-WO | 2611 ± 305 | 390 ± 32 | 178 ± 40 | 329 | 390 |
| PP-AO-MA-WO | 2525 ± 585 | 366 ± 59 | 165 ± 10 | 293 | 330 |
| PP-AO-AT | 2016 ± 324 | 267 ± 05 | 184 ± 11 | 287 | 375 |
| PP-AO-MA-AT | 2332 ± 150 | 310 ± 27 | 181 ± 10 | 280 | 376 |
| PP-AO-SWCNT | 2264 ± 283 | 392 ± 32 | 187 ± 21 | 299 | 365 |
| PP-AO-MA-SWCNT | 2719 ± 656 | 347 ± 103 | 170 ± 06 | 292 | 342 |