Table 2.

The chemical compositions of α and β phases at different positions after tension at 760 °C (wt.%).

Position	Phase	Ti	Al	V	Fe	Mo	[Mo]eq
Grip	β	83.53	3.93	4.29	3.20	5.05	17.20
	α	92.50	5.30	1.27	0.09	0.84	1.95
Tip	β	81.03	2.59	5.47	4.79	6.12	23.67
	α	92.67	5.69	0.95	0.08	0.60	1.46