. 2022 Feb 7;12(8):4656–4671. doi: 10.1039/d1ra04762k

Shifting of Raman peaks (Δω) with grain size, (X_A), Poisson's ratio (σ), anisotropy factor (A), Debye temperature (θ_D), Curie temperature (T_C) and exchange interaction (J) obtained for Ni_0.7Zn_0.2Co_0.1Fe_2−xGd_xO₄ (0 ≤ x ≤ 0.12).

Gd content (x)	Δω	X _A (nm)	σ	A (GPa)	T _C (K)	J (J) × 10⁻¹⁴	θ _D (K)
0.00	0.00	81.7 ± 1	0.30	0.53	731	2.52	685.67
0.02	27.12	56.1 ± 3.8	0.30	0.54	718	2.48	680.85
0.05	92.99	55.3 ± 1.9	0.29	0.55	715	2.47	680.85
0.07	93	50.9 ± 2.8	0.31	0.53	713	2.46	680.45
0.10	97.99	42.9 ± 0.9	0.30	0.53	712	2.45	678.01
0.12	96.86	45.0 ± 0.03	0.30	0.53	711	2.45	675.97

Shifting of Raman peaks (Δω) with grain size, (XA), Poisson's ratio (σ), anisotropy factor (A), Debye temperature (θD), Curie temperature (TC) and exchange interaction (J) obtained for Ni0.7Zn0.2Co0.1Fe2−xGdxO4 (0 ≤ x ≤ 0.12).