Table S2.
Properties and composition of sealers used in the included articles
| Sealer | Composition | Setting time | Working time | Radiopacity (mmAl) | Flow (mm) |
|---|---|---|---|---|---|
| EndoSequence BC Sealer | Zirconium oxide calcium silicates, calcium phosphate, calcium hydroxide, filler and thickening agents | 4 h | >4 h at room temperature | 6.68 | 18.45 |
| MTA fillapex | Paste A: Salicylate resin Bismuth trioxide Fumed Silica Paste B: Fumed Silica Titanium Dioxide MTA (40%) Base resin |
130 min | 35 min | 3.01 | 34.13 |
| NeoMTA plus | Powder: Tricalcium silicate, dicalcium silicate, tantalum oxide, tricalcium aluminate calcium sulfate and gypsum Liquid: Water-based gel with thickening agents and water soluble polymers |
315 min | 20 min | 3.76 | 25-29 |
| BioRoot RCS | Powder: Tricalcium silicate, zirconium dioxide, povidone Liquid: Water, calcium chloride and polycarboxylate |
4 h | 10 min | 5.2 | 16 |
| Endoseal MTA | Calcium silicates, calcium aluminates, calcium aluminoferrite, calcium sulfates, radio-opacifier, thickening agents. | 12 min | 12 min | 9.50 | 20.21 |
| AH plus | Paste A: 25%-50% bisphenol A 10%-25% zirconium dioxide NS calcium tungstate NS iron oxideleftPaste B: 2.5%-10% N, n-dibenzyl-5-oxanonandiamin-1,9 2.5%-10% amantadine | 8 h | 4 h | 10.00 | 21.87 |
| TotalFill BC sealer | Zirconium oxide Calcium silicate Calcium phosphate Calcium hydroxide Fillers and thickening agents |
4 h | Greater 4 h | 4±0.15 | 24.63 |
BC: Bioceramic, MTA: Mineral trioxide aggregate, AH: AH plus sealer, RCS: Root canal sealer