Table 3. Average Γe and Deapp Measured for the NDI0/·– Redox Couple for Zr(dcphOH-NDI)@FTO MOF Films (Standard Deviations Were Obtained from Three Samples Measured Independently for All Entries).
| DMF |
EtOH |
THF |
||||
|---|---|---|---|---|---|---|
| supporting electrolyte | Γe (mol cm–2) | Deapp (cm2 s–1) | Γe (mol cm–2) | Deapp (cm2 s–1) | Γe (mol cm–2) | Deapp (cm2 s–1) |
| LiClO4 | 5.99 ± 0.39 × 10–8 | 3.23 ± 2.16 × 10–9 | 5.95 ± 0.93 × 10–8 | 2.36 ± 1.55 × 10–10 | 6.82 ± 1.27 × 10–8 | 1.30 ± 0.24 × 10–11 |
| KPF6 | 7.92 ± 1.91 × 10–8 | 1.12 ± 0.30 × 10–9 | ||||
| TBAPF6 | 3.93 ± 1.77 × 10–8 | 6.99 ± 5.97 × 10–10 | 3.96 ± 2.82 × 10–8 | 2.80 ± 1.04 × 10–11 | ||