Comparison of the maximum sensitivity of Ho3+(Er3+)/Yb3+ doped in different material.
| Materials | Energy level | S r (K−1) | S a (K−1) | Reference |
|---|---|---|---|---|
| Bi2SiO5:Yb3+,Tm3+ | 3F3,/2/1G4 | 1.95% (300 K) | 0.0168 (300 K) | 7 |
| NaGdF4:Er3+/Yb3+ | 2H11/2/4S3/2 | 1.29% (303 K) | 0.0382 (363 K) | 28 |
| LaF3:Er3+/Yb3+ | 2H11/2/4S3/2 | 844/T−2 (150 K) | 0.0025 (400 K) | 29 |
| Y2O3:Ho3+/Yb3+/Zn3+ | 5F3/3K8 | 1067.76/T−2 (299 K) | 0.003 (673 K) | 30 |
| NaLa(MnO4)2:Sm3+/Tb3+ | 4G5/2/5D4 | 1.93 (498 K) | 0.119 (265 K) | 31 |
| BaY2Si3O10:Ho3+/Yb3+ | 5F5/5S2,5F4 | 0.49% (298 K) | 0.023 (298–448 K) | 32 |
| BaY2Si3O10:Er3+/Yb3+ | 4F9/2/2H11/2 | 0.78% (298 K) | 0.091 (298 K) | 32 |
| LaAlO3:Er3+/Yb3+ | 2H11/2/4S3/2 | 575.27/T−2 (281 K) | 0.0032 (281 K) | 33 |
| NaY(WO4)2:Er3+/Yb3+ | 2H11/2/4S3/2 | 1043.12/T−2 (133 K) | 0.0112 (515 K) | 34 |
| SrWO4:Er3+/Yb3+ | 2H11/2/4S3/2 | 1.03% (313 K) | 0.013 (513 K) | This work |
| SrWO4:Ho3+/Yb3+ | 5S2/5F4 | 1.27% (573 K) | 0.0017 (573 K) | This work |
| SrWO4:Ho3+/Yb3+ | 5S2, 5F4/5F5 | 0.41% (393 K) | 0.0158 (303 K) | This work |