. 2018 Jun 12;8(38):21460–21471. doi: 10.1039/c8ra03349h

Textural properties of ZIFC, RUFC and ZIFC@RUFC composite.

Sample	S _BET ^a/m² g⁻¹	S _mic ^b/m² g⁻¹	V _t ^c/cm³ g⁻¹	V _mic ^b/cm³ g⁻¹	D ^d/nm	N content/%
Sample	S _BET ^a/m² g⁻¹	S _mic ^b/m² g⁻¹	V _t ^c/cm³ g⁻¹	V _mic ^b/cm³ g⁻¹	D ^d/nm	CHN	XPS
ZIFC	713	603	0.41	0.31	—	7.52	7.12
RUFC	647	411	0.38	0.21	3.3	1.32	1.37
ZIFC@RUFC	982(659)^e	612(445)^e	0.70(0.39)^e	0.32(0.23)^e	4.1	1.39	1.49

Surface areas calculated using the BET equation in the relative pressure range of 0.05–0.30.

Microporous surface areas and micropore volumes calculated using the t-plot method in the thickness range of 0.4–0.6 nm.

Single point total pore volumes determined from the N₂ uptakes at relative pressures >0.995.

Mesopore diameters at the maxima of PSD curves.

The numbers in brackets are the correspondingly “hypothetical” textural parameters.