Young's modulus, tensile strength and elongation at break values of tested specimens.

	7 days	28 days	40 days
Young's modulus (N mm −2 )
A0	514.3 ± 25.0
A/P44	372.3 ± 30.3	335.9 ± 122.9	447.3 ± 73.2
A/P46	483.0 ± 53.5	406.9 ± 62.1	484.0 ± 46.9
A/P53	491.7 ± 47.4	351.4 ± 109.1	497.5 ± 71.4
A/P58	466.0 ± 74.2	498.6 ± 36.0	528.6 ± 51.9
B0	567.0 ± 25.9
B/P44	362.0 ± 52.7	368.3 ± 72.6	414.6 ± 45.5
B/P46	428.0 ± 24.2	338.7 ± 28.1	391.6 ± 77.4
B/P53	465.7 ± 55.1	370.6 ± 47.9	457.3 ± 73.3
B/P58	456.0 ± 30.6	443.8 ± 16.9	222.0 ± 55.0
Tensile strength – σ (N mm −2 )
A0	49.7 ± 8.0
A/P44	44.3 ± 6.2	31.9 ± 9.7	40.1 ± 5.6
A/P46	46.4 ± 5.0	30.7 ± 7.7	47.4 ± 2.5
A/P53	47.5 ± 7.5	34.3 ± 7.1	41.6 ± 1.6
A/P58	45.2 ± 6.4	32.5 ± 11.2	39.3 ± 8.0
B0	44.2 ± 7.2
B/P44	37.3 ± 4.0	35.0 ± 4.8	36.9 ± 8.3
B/P46	32.0 ± 6.2	30.3 ± 2.2	41.9 ± 1.6
B/P53	40.8 ± 4.9	35.5 ± 11.9	30.3 ± 3.6
B/P58	30.0 ± 5.9	44.9 ± 0.3	39.0 ± 2.2
Elongation at break – % ε
A0	1326.0 ± 225.3
A/P44	1241.3 ± 45.2	1209.0 ± 33.2	1170.0 ± 22.6
A/P46	1258.8 ± 83.2	1154.6 ± 61.4	1169.3 ± 17.7
A/P53	1166.3 ± 48.2	1102.0 ± 56.2	1187.3 ± 7.1
A/P58	1246.6 ± 21.5	1051.6 ± 57.5	1149.3 ± 35.0
B0	1021.7 ± 102.0
B/P44	674.3 ± 105.3	863.3 ± 10.7	642.6 ± 63.1
B/P46	791.0 ± 29.8	644.6 ± 41.5	1083.0 ± 219.0
B/P53	1018.6 ± 180.1	793.3 ± 81.0	653.2 ± 109.7
B/P58	780.3 ± 81.1	746.6 ± 49.7	856.0 ± 46.7