Table 2. Summary of OECT Parameters and Material Figures of Merit of the Polymers under Investigation.

polymer	μe,OECT [cm2 V–1 s–1]a	C* [F cm–3]b	μC* [F cm–1 V–1 s–1]c	gm′ [S cm–1]	Vth [mV]a
p(g7NC2N)	(2.00 ± 0.41) × 10–3	180 ± 16	0.36 ± 0.074	0.069 ± 0.012	230 ± 3.3
p(g7NC4N)	(1.46 ± 0.53) × 10–3	126 ± 12	0.18 ± 0.067	0.035 ± 0.013	210 ± 2.9
p(g7NC6N)	(2.29 ± 0.70) × 10–3	150 ± 4	0.34 ± 0.111	0.065 ± 0.019	210 ± 6.4
p(g7NC8N)	(6.01 ± 1.87) × 10–3	199 ± 27	1.19 ± 0.371	0.240 ± 0.076	250 ± 3.4
p(g7NC10N)	(1.20 ± 0.07) × 10–2	153 ± 34	1.83 ± 0.101	0.370 ± 0.023	300 ± 3.0
p(g7NC12N)(54)	(6.50 ± 1.01) × 10–3	100 ± 6	0.66 ± 0.113	0.212 ± 0.015	328 ± 5.3
p(g7NC16N)	(3.80 ± 0.59) × 10–3	86 ± 11	0.33 ± 0.074	0.047 ± 0.005	360 ± 10.0

^aμ_e,OECT OECT saturation mobility and threshold voltage (V_th) extracted from fits of I_d^1/2 vs V_G plots.

^bC* average volumetric capacitance beyond the V_th determined by electrochemical impedance spectroscopy. Reported uncertainties are one standard deviation, with n = 6 devices.

^cμC* extracted from the slope of saturated transfer curves at −0.6 V.