Table 7. Comparison of magnetocaloric effect parameters and critical exponents of indicated vdW magnetic materialsa.
| materials | field | ref | technique | –ΔSMmax | RCP | ΔTad | α | β | γ | δ | Tc | J(r) |
|---|---|---|---|---|---|---|---|---|---|---|---|---|
| Cr2Si2Te6 | H ∥ ab | (287) | MH | 4.9 | ||||||||
| H ∥ c | MH | 5.05 | 114 | |||||||||
| (288) | MAP | 0.170(8) | 1.532(1) | 10.01(5)cal | 30.95(20) | r–3.630 | ||||||
| KFP | 0.175(9) | 1.562(9) | 9.93(6)cal | 30.97(16) | ||||||||
| CI | 9.917(8) | 31 | ||||||||||
| (287) | MAP | 0.169(4) | 1.33(8) | 8.9(3)cal | 32.0(4) | |||||||
| KFP | 0.178(9) | 1.32(4) | 8.4(2)cal | 32.2(4) | ||||||||
| CI | 9.28(3) | 32 | ||||||||||
| Cr2Ge2Te6 | H ∥ ab | (287) | MH | 2.6 | ||||||||
| H ∥ c | MH | 2.64 | 87 | |||||||||
| (289) | MH | 3.21 | 94.3 | |||||||||
| (279) | MAP | 0.196(3) | 1.32(5) | 7.73(15)cal | 62.65(7) | r–3.52 | ||||||
| KFP | 0.200(3) | 1.28(3) | 7.40(5)cal | 62.70(12) | ||||||||
| CI | 7.96(1) | 62.7 | ||||||||||
| (280) | MEC | 0.177(9) | 1.746(8) | 10.869(5)cal | 66.4(3) | r–3.592 | ||||||
| (290) | MAP | 0.242(6) | 0.985(3) | 5.070(6)cal | 67.93(7) | |||||||
| KFP | 0.240(6) | 1.000(5) | 5.167(6)cal | 67.90(8) | ||||||||
| CI | 5.032(5) | 67.9 | ||||||||||
| (291) | AC | 0.35 | 1.43 | 5.24 | 62.84 | |||||||
| CrI3 | H ∥ ab | (292) | MH | 2.68 | ||||||||
| H ∥ c | MH | 4.24 | 122.6 | |||||||||
| SH | 5.65 | 2.34 | ||||||||||
| (293) | MAP | 0.284(3) | 1.146(11) | 5.04(1)cal | 60.42(8) | r–4.69 | ||||||
| KFP | 0.260(4) | 1.136(6) | 5.37(4)cal | 60.24(26) | ||||||||
| CI | 5.32(2) | 60 | ||||||||||
| (294) | MAP | 0.325(6) | 0.825(3) | 3.538(6)cal | 64.02(7) | |||||||
| KFP | 0.323(6) | 0.835(5) | 3.585(6)cal | 63.99(9) | ||||||||
| CI | 3.569(4) | 64 | ||||||||||
| SH | 0.11 | |||||||||||
| CrBr3 | H ∥ c | (295) | MH | 7.2 | 191.5 | |||||||
| SH | 6.91 | 2.37 | ||||||||||
| CrCl3 | H ∥ ab | (296) | MH | 14.6 | 340.3 | |||||||
| H ∥ c | MH | 13.8 | 317.3 | |||||||||
| H ∥ ab | (297) | MH | 19.8 | |||||||||
| H ∥ c | MH | 19.5 | ||||||||||
| SH | 6.8 | |||||||||||
| H ∥ ab | (296) | MAP | 0.26(1) | 0.86(1) | 4.31(9)cal | 19.11(10) | ||||||
| KFP | 0.28(1) | 0.89(1) | 4.18(8)cal | 19.18(37) | ||||||||
| CI | 4.6(1) | 19 | ||||||||||
| VI3 | H ∥ ab | (298) | MH | 2.27 | ||||||||
| H ∥ c | MH | 2.64 | ||||||||||
| SH | 2.80 | 0.96 | ||||||||||
| H ∥ ab | (299) | MH | 2 | |||||||||
| H ∥ c | MH | 3 | ||||||||||
| (298) | MAP | 0.244(5) | 1.03(1) | 5.21(4)cal | 50.04(10) | |||||||
| CI | 5.24(2) | 50 | ||||||||||
| (299) | MEC | 0.204(8) | 1.65(7) | 9.09(1)cal | ||||||||
| MAP | 0.155(7) | 1.04(2) | 7.70(9)cal | 45.31(13) | ||||||||
| KFP | 0.146(1) | 1.07(7) | 8.32(8)cal | 45.32(12) | ||||||||
| CI | 7.78(8) | 45 | ||||||||||
| AC | 0.12(3) | 0.92(4) | 8.30(4) | |||||||||
| Fe2.64GeTe2 | H ∥ ab | (300) | MH | 1.26 | ||||||||
| H ∥ c | MH | 1.44 | 113.3 | |||||||||
| SH | 1.20 | 0.66 | ||||||||||
| (301) | MAP | 0.374(1) | 1.273(8) | 4.404(12)cal | 151.27(1) | r–4.89 | ||||||
| KFP | 0.372(4) | 1.265(15) | 4.401(6)cal | 151.25(5) | ||||||||
| CI | 4.50(1) | 151 | ||||||||||
| Fe2.72GeTe2 | H ∥ c | (302) | MEC | 0.361(3) | 1.736(7) | 5.806(8) | 157.2(2) | |||||
| H ∥ ab | MEC | 0.714(3) | 1.243(7) | 2.741(1) | 158.5(2) | |||||||
| Fe2.85GeTe2 | H ∥ c | (303) | MAP | 0.361(2) | 1.225(2) | 4.39(1)cal | 193.68(26) | r–4.8 | ||||
| KFP | 0.363(4) | 1.228(4) | 4.38(3)cal | 193.77(11) | ||||||||
| CI | 4.41(3) | 194 | ||||||||||
| Fe3GeTe2 | H ∥ c | (304) | MAP | 0.327(3) | 1.079(5) | 4.30(5)cal | 215.13(8) | r–4.6 | ||||
| KFP | 0.322(4) | 1.063(8) | 4.30(7)cal | 215.15(21) | ||||||||
| CI | 4.261(9) | 215 | ||||||||||
| Fe5GeTe2 | H ∥ c | (305) | MAP | 0.351(1) | 1.413(5) | 5.02(6)cal | 273.82(10) | r–4.916 | ||||
| KFP | 0.346(4) | 1.364(9) | 4.94(0)cal | 273.86(19) | ||||||||
| CI | 5.02(1) | 274 | ||||||||||
| t-Cr5Te8 | H ∥ ab | (306) | MH | 1.39 | ||||||||
| H ∥ c | MH | 1.73 | 131.2 | |||||||||
| (307) | MAP | 0.314(7) | 1.83(2) | 6.83(7)cal | 230.76(9) | r–4.626 | ||||||
| KFP | 0.315(7) | 1.81(2) | 6.75(6)cal | 230.65(26) | ||||||||
| CI | 6.35(4) | 230 | ||||||||||
| (308) | MAP | 0.362 | 1.399 | 4.86cal | 220.1 | r–4.949 | ||||||
| CI | 4.83 | 220 | ||||||||||
| m-Cr5Te8 | H ∥ c | (309) | MAP | 0.327(4) | 1.26(1) | 4.9(1)cal | 221.82(44) | r–4.94 | ||||
| KFP | 0.321(7) | 1.27(2) | 4.9(2)cal | 221.7(7) | ||||||||
| CI | 4.86(4) | 222 | ||||||||||
| MH | 2.38 | 143 | ||||||||||
| Cr4Te5 | H ∥ c | (310) | MH | 2.42 | ||||||||
| H ∥ ab | MH | 2.58 | ||||||||||
| MAP | 0.388(4) | 1.290(8) | 4.32(3)cal | 318.88(24) | r–4.85 | |||||||
| KFP | 0.387(9) | 1.288(5) | 4.32(2)cal | 318.74(26) | ||||||||
| CI | 3.93(8) | 318.7 | ||||||||||
| FeCr2Te4 | H ∥ c | (311) | MH | 1.92 | ||||||||
| MAP | 0.33(2) | 1.20(1) | 4.6(2)cal | 122.8(4) | r–4.88 | |||||||
| KFP | 0.30(1) | 1.22(1) | 5.1(1)cal | 122.6(7) | ||||||||
| CI | 4.83(6) | 123 | ||||||||||
| Mn3Si2Te6 | H ∥ c | (312) | SH | 2.94 | 1.14 | |||||||
| H ∥ ab | MH | 2.53 | ||||||||||
| (312) | MAP | 0.41(1) | 1.25(1) | 4.05(5)cal | 74.23(4) | |||||||
| KFP | 0.41(1) | 1.21(2) | 3.95(2)cal | 74.27(15) | ||||||||
| CI | 4.29(5) | 74 | ||||||||||
| Cr0.33NbS2 | H ∥ c | (313) | MAP | 0.370(4) | 1.380(2) | 4.729(7)cal | 126.3(7) | r–4.9 | ||||
| CI | 4.853(6) | 126 | ||||||||||
| (314) | KFP | 0.346(40) | 1.344(2) | 4.88(44)cal | 130.78(8) | |||||||
| Fe0.26TaS2 | H ∥ c | (315) | MAP | 0.460(4) | 1.216(11) | 3.64(3)cal | 100.67(3) | r–4.71 | ||||
| KFP | 0.459(6) | 1.205(11) | 3.63(4)cal | 100.69(5) | ||||||||
| CI | 3.69(1) | 100.7 |
a
The MEC, SH, MAP, KFP, and CI represent the magnetic entropy change, specific heat, modified Arrott plot, Kouvel–Fisher plot, and critical isotherm, respectively.