Table 3.
Range of mechanical properties of agar biopolymer films (±standard deviation).
| Property Range | Young’s Modulus (MPa) | Elongation at Break (%) | Ultimate Tensile Strength (MPa) | Agar (%) | Gly (%) |
|---|---|---|---|---|---|
| Elongation at break (Min) | 4.59 ± 1.21 | 3.92 ± 1.33 | 8.48 ± 2.69 | 2.00 | 0.31 |
| Elongation at break (Max) | 0.08 ± 0.03 | 115.80 ± 12.75 | 2.71 ± 0.45 | 4.00 | 10.70 |
| Ultimate tensile strength (Min) | 0.03 ± 0.00 | 28.66 ± 0.00 | 0.11 ± 0.00 | 1.00 | 10.70 |
| Ultimate tensile strength (Max) | 13.24 ± 1.92 | 14.68 ± 2.72 | 39.11 ± 4.02 | 1.00 | 0.28 |
| Young’s modulus (Min) | 0.03 ± 0.00 | 28.66 ± 0.00 | 0.11 ± 0.00 | 1.00 | 10.70 |
| Young’s modulus (Max) | 13.24 ± 1.92 | 14.68 ± 2.72 | 39.11 ± 4.02 | 1.00 | 0.28 |