Table 4.

Overview of all the relevant parameters obtained after the mechanical test and data processing from each sample group tested.

Specimen Group	Specimen n°	σ 1st Failure (MPa)	ε 1st Failure	Work 1st Failure (MPa)	σmax (GPa)	ε max	Work TOT (MPa)	Young's Modulus (MPa)
	1	32.1	0.032	0.562	34.3	0.060	0.948	1040.00
	2	32.0	0.031	0.412	34.9	0.060	0.456	795.59
ABS	3	32.1	0.034	0.575	36.6	0.060	1.044	977.04
	4	29.2	0.028	0.418	34.8	0.059	0.891	1050.90
	5	34.0	0.033	0.605	38.0	0.060	1.246	1062.10
	Average	31.9	0.032	0.515	35.7	0.060	0.917	985.13
	Std Dev	1.5	0.002	0.082	1.4	0.001	0.260	99.25
	1	88.0	0.023	1.019	92.9	0.039	1.693	1040.00
	2	78.2	0.028	0.847	85.2	0.033	0.943	795.59
PLA	3	80.0	0.021	0.917	85.4	0.033	0.941	977.04
	4	75.3	0.017	0.658	89.0	0.029	0.944	1050.90
	5	80.1	0.019	0.843	89.0	0.033	1.560	1062.10
	Average	80.3	0.022	0.857	88.3	0.033	1.216	985.13
	Std Dev	4.2	0.004	0.118	2.8	0.003	0.338	99.25
	1	42.1	0.042	0.900	43.6	0.120	2.248	1230.00
	2	42.0	0.043	1.072	42.7	0.094	1.619	1160.00
PETG	3	42.2	0.043	1.024	43.2	0.074	1.289	1198.00
	4	41.0	0.043	1.055	41.9	0.086	1.594	1139.00
	Average	41.8	0.043	1.013	42.9	0.094	1.688	1181.75
	Std Dev	0.5	0.000	0.068	0.6	0.017	0.349	34.97
	1	8.5	0.034	0.153	18.5	0.127	0.488	250.77
	2	10.7	0.034	0.206	18.8	0.127	0.719	300.02
POLY_FFF	3	8.5	0.036	0.172	15.7	0.127	0.496	238.88
	4	8.0	0.035	0.155	15.1	0.128	1.327	228.65
	5	8.2	0.037	0.167	15.0	0.128	0.448	218.65
	Average	8.8	0.035	0.171	16.6	0.127	0.696	247.39
	Std Dev	1.0	0.001	0.019	1.7	0.000	0.330	28.39
	1	50.4	0.027	0.513	53.0	0.097	1.584	1308.03
	2	55.0	0.024	0.331	59.6	0.096	1.540	1555.05
POLY_BASIC	3	55.2	0.027	0.435	63.0	0.096	1.444	1454.20
	4	55.1	0.027	0.547	67.3	0.097	1.468	1377.40
	5	55.0	0.026	0.483	64.9	0.096	4.027	1415.10
	Average	54.2	0.026	0.462	61.6	0.096	2.013	1421.96
	Std Dev	1.9	0.001	0.075	5.0	0.000	1.008	82.18