Table 5.

Dynamic mechanical properties of compression molded sheets and 3D printed samples.

Sample	E’ (GPa) at 40 °C	E’ (GPa) at 60 °C	E” (MPa) 1	Tg, Tan δ 2 (°C)	Tan δ 2	N (mol/m3)	A	C	r
PLA-N-C	2.91	0.48	0.38	65.6	2.33	2.89 × 104
PLA-N-B45	2.65	0.46	0.35	65.6	1.74	2.76 × 104
PLA-N-B60	2.56	0.38	0.37	65.0	1.42	2.31 × 104
PLA-P-C	3.21	0.43	0.38	65.8	2.47	2.58 × 104	0.12	1.23	2.01
PLA-P-B45	2.66	1.07	0.45	64.4	0.76	6.41 × 104		0.43	0.02
PLA-P-B60	2.72	1.24	0.39	63.2	0.43	7.48 × 104		0.33	1.23
PLA-CF-C	5.00	0.77	0.75	64.8	1.77	4.63 × 104	−0.12	1.07	5.13
PLA-CF-B45	5.56	1.32	0.73	65.9	1.66	7.93 × 104		0.73	7.82
PLA-CF-B60	5.68	1.38	0.92	65.6	1.52	8.29 × 104		0.61	8.72
PLA-Cu-C	3.13	0.62	0.48	64.7	1.19	3.73 × 104	0.52	0.83	0.12
PLA-Cu-B45	1.57	0.74	0.26	65.2	0.65	4.45 × 104		0.37	−0.62
PLA-Cu-B60	1.74	0.99	0.26	64.5	0.41	5.96 × 104		0.26	−0.49

¹ Peak of loss modulus. ² Peak of Tan δ.