Table 3.
Biomechanical properties of the native and decellularized biological tissues 1.
| Thickness (mm) | E (MPa) | FS (%) | UTS (MPa) | I (MPa) | |
|---|---|---|---|---|---|
| NBPs | 0.29 ± 0.04 | 8.54 ± 3.33 | 108.61 ± 20.79 | 31.64 ± 6.93 | 17.08 ± 6.22 |
| DBPs | 0.28 ± 0.06 | 8.72 ± 4.49 | 103.056 ± 19.82 | 26.11 ± 8.76 | 13.85 ± 5.58 |
| NPPs | 0.14 ± 0.03 | 15.23 ± 9.06 | 82.34 ± 37.65 | 15.61 ± 6.1 | 7.66 ± 4.35 |
| DPPs | 0.13 ± 0.02 | 12.71 ± 3.51 | 98.29 ± 20.52 | 19.21 ± 5.17 | 10.23 ± 4.35 |
1 Thickness (mm), Young’s modulus (E, MPa), failure strain (FS, %), ultimate tensile strength (UTS, MPa), and toughness (I, MPa) are reported. Data are expressed as mean ± SD.