Table 1.

Various properties of the PTMO_x–T6A6T copolymers

	HS (wt%)	ηinh (dl/g)	Tg (°C)	Tflexa (°C)	Tflowb (°C)	G′-mod (Mpa)	E-mod (Mpa)	CS25% (%)	TS50%c (%)
PTMO650	43.8	1.8	−45	35	200	102	311	17	32
PTMO1000	34.2	2.5	−60	−15	185	51	133	14	28
PTMO1400	27.1	1.5	−65	0	180	30	87	11	18
PTMO2000	21.1	2.9	−70	10	185	18	46	9	11
PTMO2900	15.7	3.5	−70	20	175	9	29	7	8

^aT_flex is the temperature at onset of the tuber plateau as measured by DMTA [28]

^bT_flow is the temperature where the material starts to flow as measured by DMTA [28]

^cThe TS at 50% strain as measured by the staircase loading test