Percentage improvement in UTS, K_IC and flexural modulus for epoxy reinforced with aerographene.

Resin	Filler			Composite fabrication	UTS (%)	K IC (%)	Flex mod. (%)	Ref./year
	Type	Synthesis	Loading
ML-523 and HA-11	3D nitrogen doped graphene	GO + dicyanamide hydrothermal reduction	0.1 wt%	Ultrasonic mixing	19			2020 (ref. 177)
LY 1556 and XB 3471 100 : 12	Ultra large-GA	Directional freeze drying of GO	0.11 vol%	Vacuum infiltration		69		2018 (ref. 178)
	Small-GA		0.16 vol%			33
Epoxy and hardener	Multilayer graphene web	CVD on Ni template	8.3 wt%	Vacuum infiltration		100		2018 (ref. 179)
LY1556 and TETA in 100 : 12	Non-oxidized graphene aerogel	Bi-directional freeze casting in PVA	0.45 vol%	Vacuum infiltration		76		2018 (ref. 176)
			0.34 vol%				25
Aeromarine 300/21	Commercial GF		0.13 wt%	Mold casting	12			2017 (ref. 180)
Rim 135 and Rim 137 100 : 30	Aero-graphite	CVD on ZnO template	0.45 wt%	Vacuum infiltration		19		2016 (ref. 181)
Epoxy and hardener	GA	Reduction using HI, freeze drying	1.4 wt%	Vacuum infiltration		64		2015 (ref. 182)
			0.5 wt%				12
LY1556 and TETA 100 : 12	GF	CVD on Ni template	0.1 wt%	Vacuum infiltration		70		2014 (ref. 183)
			0.2 wt%				53