. 2022 Aug 26;89:106139. doi: 10.1016/j.ultsonch.2022.106139

Table 2.

The Scheil solidification sequences obtained from the thermodynamic calculation.

0.7Fe alloy 1.2Fe alloy
1 L L
2 L → α-Al L → Al3Fe
3 L → α-Al + Al3Fe L → α-Al + Al3Fe
4 L + Al3Fe → α-Al + Al6Fe L + Al3Fe → α-Al + Al6Fe
5 L → α-Al + Al6Fe L → α-Al + Al6Fe
6 L + Al6Fe → α-Al + β-Fe L + Al6Fe → α-Al + β-Fe
7 L → α-Al + β-Fe L → α-Al + β-Fe
8 L + β-Fe → α-Al + α-Fe L + β-Fe → α-Al + α-Fe
9 L → α-Al + α-Fe L → α-Al + α-Fe
10 L → α-Al + α-Fe + Al2Cu L → α-Al + α-Fe + Al2Cu
11 L → α-Al + Mg2Si + Al2Cu L → α-Al + Mg2Si + Al2Cu
12 L → α-Al + Mg2Si + Al2Cu + Al2CuMg L → α-Al + Mg2Si + Al2Cu + Al2CuMg