Table 2.

Glass transition temperature (T_g) and heat capacity jump (ΔC_p). VBzGG-m amount: 1 wt%.

Macromonomer	Material	Tg, °C	ΔCp, J/g °C
VBzGG-1	PSt extracted	92.4	1.71
	PSt-VBzGG-1 SIPN	87.2	1.03
	PSt-l-VBzGG-1	105.7	2.15
VBzGG-3	PSt extracted	91.3	0.60
	PSt-VBzGG-3 SIPN	95.7	0.59
	PSt-l-VBzGG-3	107.1	1.69
VBzGG-5	PSt extracted	88.7	0.49
	PSt-VBzGG-5 SIPN	97.0	0.90
	PSt-l-VBzGG-5	107.0	2.12
VBzGG-7	PSt extracted	91.5	1.04
	PSt-VBzGG-7 SIPN	64.7	1.24
	PSt-l-VBzGG-7	106.8	1.17
VBzGG-10	PSt extracted	89.8	0.35
	PSt-VBzGG-10 SIPN	96.0	0.69
	PSt-l-VBzGG-10	106.6	0.88
Linear PSt	synthesized at the same conditions	94.3	0.88
	formed in the presence of GG	93.4	0.35