| interface stiffness for
mode I, Knn(MPa/mm) |
158 823 |
|
| interface stiffness for
mode II, Kss(MPa/mm) |
158 823 |
|
| interface stiffness for
mode III, Ktt(MPa/mm) |
158 823 |
|
| interface strength for mode
I, Nmax (MPa) |
69.3 |
ASTM D638 |
| interface strength for mode
II, Tmax (MPa) |
69.3 |
|
| interface
strength for mode
III, Smax (MPa) |
69.3 |
|
| interlaminar
fracture toughness
for mode I, GIc(mJ/mm2) |
0.36 |
ASTM D5528 |
| interlaminar fracture toughness
for mode II, GIIc(mJ/mm2) |
1.4 |
ASTM D7905 |
| interlaminar fracture toughness
for mode III, GIIIc(mJ/mm2) |
1.4 |
|
| material
constant, η |
1.45 |
|
| density, ρ (kg/m3) |
1100 |
|