| tensile and compression
modulus along 1 direction, E1+/– (GPa) |
51.2 |
ASTM D3039 |
| tensile and compression
modulus along 2 direction, E2+/– (GPa) |
47.8 |
ASTM D3039 |
| poisson’s
ratio,
υ12
|
0.3 |
ASTM D3039 |
| shear modulus, G12 (GPa) |
3000.5 |
ASTM D3518 |
| longitudinal tensile strength, XT (MPa) |
580.4 |
ASTM D3039 |
| longitudinal
compressive
strength, XC (MPa) |
434.2 |
ASTM D6641 |
| transverse tensile strength, YT (MPa) |
484.3 |
ASTM D3039 |
| transverse compressive strength, YC (MPa) |
381.7 |
ASTM D6641 |
| shear strength, S (MPa) |
89.5 |
ASTM D3518 |
| density, ρ (kg/m3) |
1650 |
|
| thickness, T (mm) |
0.25 |
|
| fiber tensile energy release
rate, GftC(mJ/mm2) |
35.1 |
ASTM D5045 |
| fiber compressive energy
release rate, GfcC(mJ/mm2) |
15.2 |
|
| matix tensile energy release
rate, GmtC(mJ/mm2) |
35.4 |
ASTM D5045 |
| matrix compressive energy
release rate, GmcC(mJ/mm2) |
14.9 |
|
| effective yield stress,
σ̃y0 (MPa) |
81.0 |
ASTM D3518 |
| hardening constant, C
|
0 |
|
| power
index, p
|
0 |
|