Table 2. Internal Quantum Efficiency of the (Al1–xGax)2O3:Mn4+ Samples (Calcined at 1773 K) Measured at 320 nm Excitation at Room Temperature.

sample composition (x value) QE, %
0 22.6 ± 1.0
0.05 20.6 ± 0.5
0.1 16.1 ± 1.0
0.15 18.2 ± 1.0
≥0.2 low, not measured