Table 10.

Experimentally determined mechanical properties for the CPE CF112 Carbon material.

Test Type	Specimen Type	Mechanical Property
Tensile test	XY Specimens	Tensile modulus—4448.10 MPa
		Tensile stress at yield (0.2%)—40.26 MPa
		Ultimate tensile stress—47.29 MPa
		Tensile strain at tensile strength—1.85%
		Poisson’s ratio—0.388
Tensile test	XZ1 Specimens	Tensile modulus—4783.22 MPa
		Tensile stress at yield (0.2%)—38.86 MPa
		Tensile stress at tensile strength—44.97 MPa
		Tensile strain at tensile strength—1.64%
		Poisson’s ratio—0.316
Tensile test	XZ2 Specimens	Tensile modulus—3175.97 MPa
		Tensile stress at yield (0.2%)—29.56 MPa
		Tensile stress at tensile strength—31.50 MPa
		Tensile strain at tensile strength—1.38
		Poisson’s ratio—0.225
Compression test	-	Flatwise compressive modulus—3184.90 MPa
		Compression stress at yield (0.2%)—29.48 MPa
		Ultimate compression strain—31.40 MPa
		Strain at ultimate compression strain—1.38%