Table 1.

The results of the characterisation of materials in the form of: P—raw polymer, C—solvent cast composite plate, R—thermally extruded rods. TGA: filler content; GPC: M_n—number average molecular weight, M_w—weight average molecular weight, PDI—polydispersity index; DSC (second heating): $T_g$—transition temperature, $T_{ccr}$—cold crystallisation temperature, $H_{ccr}$—cold crystallisation enthalpy, $T_m$—melting temperature, $H_m$—melting enthalpy, $\Delta H/w$—enthalpy of crystalline phase in the polymeric matrix of the sample, $w$—content of polymer in the sample.

Material	Form	Filler Content ± SD [%]	Mn [kDa]	Mw [kDa]	PDI	${\mathit{T}}_{\mathit{g}}$ [°C]	${\mathit{T}}_{\mathit{c}\mathit{c}\mathit{r}}$ [°C]/$\Delta {\mathit{H}}_{\mathit{c}\mathit{c}\mathit{r}}$ [J/g]	${\mathit{T}}_{\mathit{m}}$ [°C]/$\Delta {\mathit{H}}_{\mathit{m}}$ [J/g]	$\Delta \mathit{H}/\mathit{w}$ [J/g]
PCL-1010-BH	P		125.7	229.0	1.8	−61.6	-	57.9/59.3	59.3
	C	19.9 ± 0.2	126.8	198.8	1.6	−63.0	-	56.2/51.7	64.5
	R	19.8 ± 0.6	120.1	195.9	1.6	−62.9	-	57.0/53.5	66.6
PLC70-1010-BH	P		99.1	173.4	1.7	30.3	128.0/1.7	159.8/1.8	0.1
	C	19.7 ± 0.4	84.7	161.9	1.8	30.1	106.4/14.8	158.8/15.4	0.7
	R	20.1 ± 1.2	64.2	142.2	2.2	26.9	89.8/17.2	160.0/18.6	1.8
PLC85-1010-BH	P		71.9	228.4	3.2	42.5	-	-	0.0
	C	19.3 ± 0.6	73.7	228.3	3.1	42.1	-	-	0.0
	R	19.9 ± 0.3	58.8	207.0	3.5	42.6	-	-	0.0
PLG82-1010-BH	P		122.8	220.2	1.8	58.7	-	-	0.0
	C	19.8 ± 0.5	125.2	227.7	1.8	57.0	-	-	0.0
	R	19.8 ± 0.4	56.5	151.1	2.7	54.6	-	-	0.0