Table 1.

The HER parameters, Tafel slopes and estimated electrochemically active surface area for the obtained catalysts.

Electrode	Overpotential (mV vs. RHE) to achieve a current density of −10 mA cm−2	Onset potential (mV vs. RHE)	b (mV dec−1)	Estimated ECSA (cm2) (0.04 mF cm−2)
Pt	92	−75	38	–
TiO2	Does not achieve	–	330	–
TiO2/SrMoO4	313	−275	152	85.5
TiO2/CoMoO4	242	−219	168	65.25
TiO2/SrMoO4/CoMoO4	167	−209	91	140
TiO2/SrMoO4/GO	146	−96	62	221
TiO2/CoMoO4/GO	184	−121	75	212.75
TiO2/SrMoO4/CoMoO4/GO	121	−60	90	296.25