. 2022 Dec 25;13(1):104. doi: 10.3390/nano13010104

Table 1.

Synthetic conditions and pore parameters of siliceous NPs under study ^a.

Entry	Sample	T/°C; t/h	d_TEM^b/nm	S_BET^c/m² g⁻¹	V_p^d/cm³ g⁻¹	d_p^e/nm	d_p,peak^f/nm
1	MSN	80; 2	81.9 ± 7.9	882.5	2.04	6.42	2.53
2	E-PMO	50; 6	104.4 ± 14.4	1082.3	1.45	3.71	2.82
3	E-PMO	80; 2	120.2 ± 19.8	904.3	0.73	2.58	2.53
4	P-PMO	50; 6	120.1 ± 22.6	1300.0	1.46	3.28	2.00
5	P-PMO	80; 2	105.4 ± 4.9	1654.0	1.34	2.52	2.26

^a see the Section 2 and Supplementary Materials for the formulations in the material preparation. ^b Particle diameter determined using TEM observation. ^c Specific BET surface area. ^d BJH adsorption cumulative pore volume. ^e BJH average pore diameters calculated using the Barrett−Joyner−Halenda method. ^f The peaks seen on the BJH pore size distribution graph (Figure 1F).