Table 4.

Electrochemical performance of some MXene-based flexible SCs

Electrode	Electrolyte	Capacitance	Stability	Refs.
Ti3C2Tx films	1 M H2SO4	245 F/g at 2 mV/s	100% after 10,000 cycles	[182]
Ti3C2Tx-Li film	1 M H2SO4	892 F/cm3 at 2 mV/s	100% after 10,000 cycles	[183]
MXene/rHGO	3 M H2SO4	1445 F/cm3 at 2 mV/s	93% after 10,000 cycles	[184]
MXene/rGO-5 wt.%	1 M KCl	1040 F/cm3 at 2 mV/s	100% after 20,000 cycles	[86]
MXene/graphene	3 M H2SO4	127 F/g at 2 mV/s	95.7% after 10,000 cycles	[185]
layered Ti3C2/PPy	PVA/H2SO4	35.6 mF/cm2 at 0.3 mA/cm2	100% after 10,000 cycles	[186]
Ti3C2Tx/PANI	1 M H2SO4	272.5 F/g at 1 A/g	71.4% after 4000 cycles	[187]
Ti3C2Tx/PEDOT:PSS	1 M H2SO4	1065 F/cm3 at 2 mV/s	80% after 10,000 cycles	[188]
Mo1.33C MXene/PEDOT:PSS	1 M H2SO4	1310 F/cm3 at 2 mV/s	90% after 10,000 cycles	[189]
Ti3C2Tx/MnO2	1 M Na2SO4	130.5 F/g at 0.2 A/g	100% after 1000 cycles	[190]