Table 3. Release % in GA, POLY, and ANTO Solutions for Silicon, Calcium, and Cerium.

	GA		POLY		ANTO
BG	fine	coarse	fine	coarse	fine	coarse	element
H0	2.3	0.5	2.6	0.8	1.3	0.9	silicon
H1.2	1.5	0.7	2.3	0.5	N.A.a	N.A.a
H3.6	2.1	0.5	2.3	0.7	N.A.a	N.A.a
H5.3	2.1	0.6	2.5	0.8	1.0	0.7
K0	2.0	0.6	2.1	0.8	1.0	0.7
K1.2	1.9	0.5	2.0	0.5	0.9	0.5
K3.6	1.6	0.5	1.0	0.5	N.A.a	N.A.a
K5.3	2.4	0.5	2.5	0.4	N.A.a	N.A.a
MBG	1.2	1.0	1.0	0.8	1.2	1.1
MBG1.2	1.1	1.0	1.1	1.4	1.1	1.0
MBG3.6	1.3	1.2	1.2	1.2	1.1	1.0
MBG5.3	1.4	1.2	1.5	1.4	1.4	1.1
H0	2.2	0.8	1.6	0.5	1.5	1.4	calcium
H1.2	2.2	0.7	1.5	0.6	N.A.a	N.A.a
H3.6	2.3	0.8	1.7	0.5	N.A.a	N.A.a
H5.3	2.3	0.6	1.8	0.6	1.3	1.0
K0	2.4	1.6	1.7	2.3	1.2	1.3
K1.2	2.3	1.6	1.5	1.2	1.2	1.2
K3.6	2.4	1.5	1.0	2.9	N.A.a	N.A.a
K5.3	2.7	1.6	2.8	2.4	N.A.a	N.A.a
MBG0	8.3	7.5	4.8	4.9	4.0	3.1
MBG1.2	7.9	7.1	5.0	5.1	4.3	3.8
MBG3.6	6.7	6.2	4.6	3.9	4.4	4.1
MBG5.3	7.0	6.4	5.0	4.8	4.0	4.5
H0							cerium
H1.2	0.5	0.1	0.4	0.3	N.A.a	N.A.a
H3.6	0.3	0.0	0.1	0.0	N.A.a	N.A.a
H5.3	0.3	0.0	0.1	0.0	0,1	0.1
K0
K1.2	0.0	0.0	0.1	0.1	0.0	0.0
K3.6	0.0	0.0	0.0	0.0	N.A.a	N.A.a
K5.3	0.0	0.0	0.0	0.0	N.A.a	N.A.a
MBG0
MBG1.2	0.0	4.6	2.6	2.9	0.2	0.2
MBG3.6	1.2	1.6	0.6	0.4	0.3	0.1
MBG 5.3	0.5	0.3	0.6	0.1	0.2	0.1

^aNot assessed (N.A.).