Table 7.
Principal properties of SLS investigations. With * the compression, ** tensile and *** flexural modulus/strength. (not filled cells mean no data).
| Composite | Modulus (MPa) | Strength (MPa) | Strain at Break (%) | Porosity | Pore Size (µm) | Particle Size (µm) | Content (wt%) | Technique | By |
|---|---|---|---|---|---|---|---|---|---|
| PDLLA | 68.07 *** | 1 *** | 22 *** | 150–300 | 0 | SLS | [167] | ||
| PDLLA/58S | 79 *** | 1.7 *** | 6 *** | 150–300/12.5 | 10 | ||||
| PDLLA/58S | 21 *** | 0.6 *** | 4 *** | 150–300/12.5 | 20 | ||||
| PDLLA/58S | 10 *** | 0.2 *** | 3 *** | 150–300/12.5 | 30 | ||||
| PCL | 86 ** | 4.4 ** | 10 | 50 | SLS | [168] | |||
| PCL/β-TCP | 124 ** | 2 ** | 3 | 50/3–5 | 10 | ||||
| PCL/β-TCP | 117 ** | 1.2 ** | 1.7 | 50/3–5 | 50 | ||||
| PLDLA | 68 *** | 3.7 *** | 23 *** | 38 | 200 | SLS | [169] | ||
| PLDLA/58S | 79 *** | 2.4 *** | 6.9 *** | 26 | 200 | 12.15 | 10 | ||
| PLDLA/58S | 21 *** | 0.5 *** | 4 *** | 27 | 200 | 12.15 | 20 | ||
| PLDLA/58S | 10 *** | 0.3 *** | 7.4 *** | 30 | 200 | 12.15 | 30 | ||
| PLLA | 1800 * | 20.8 * | 400 | SLS | [172] | ||||
| PLLA/mBG | 3100 * | 50.2 * | 400 | 0.5 | 5 | ||||
| PLLA/p-mBG | 3600 * | 62.9 * | 400 | 0.5 | 5 | ||||
| PGPL-DEX | 95 * | 6.2 * | 40.4 | 450 | SLS | [173] | |||
| PGPL-DEX/mBG | 230 * | 12.1 * | 40.4 | 450 | 15 | ||||
| PGPL-DEX/ p-mBG | 270 * | 17.5 * | 40.4 | 450 | 15 | ||||
| PLA | 890 * | 10.5 * | 400 | SLS | [174] | ||||
| PLLA/mBG | 1100 * | 15.1 * | 400 | 0.4 | 4 | ||||
| PLLA/Ag-mBG | 1180 * | 15.9 * | 400 | 0.4 | 4 | ||||
| SA/13-93 | 20.4 * | 50.3 | 300–800 | 42.08 | 100 | SLS | [175] | ||
| SA/13-93 | 41 * | 40 | 300–800 | 16 | 100 | SLS | [176] |